退火气氛对铝诱导a-Si薄膜结晶过程的影响
" q3 J" k0 J1 S4 o1 f( F3 u: D  
( R& j/ i* G* V% p3 _
  Q2 p' ^1 `* ^4 R& Y2 n3 u
$ I9 d- i1 q+ f0 o8 s. A% o
5 o# T" I8 @7 {# q) l/ z8 \【英文篇名】 An Experimental Study of Aluminum-Induced Crystallization of Amorphous Silicon Thin Film in Different Atmospheres
: k/ p8 q7 T. o. \* A4 `% Z【作者中文名】 王成龙; 范多旺; 孙硕; 张福甲;
! i3 N: {1 A$ |6 [- G0 H: f【作者英文名】 Wang Chenglong1; 2; Fan Duowang1; Sun Shuo3; and Zhang Fujia3(1 National Engineering Research Center for Technology and Equipment of Environmental Deposition; Lanzhou 730070 China)(2 MOE Key Laboratory of Opto-Electronic Technology and Intelligence Control; Lanzhou Jiaotong University; Lanzhou 730070; China)(3 School of Physics Science and Technology; Lanzhou University; Lanzhou 730000; China); ) L' T  |3 ^! y2 i: y8 u1 v
【作者单位】 国家绿色镀膜技术与装备工程技术研究中心; 兰州大学物理科学与技术学院; 兰州大学物理科学与技术学院 兰州730070兰州交通大学光电技术与智能控制教育部重点实验室; 兰州730070兰州交通大学光电技术与智能控制教育部重点实验室; ' a1 e, I( b; z6 ^! u% N
【文献出处】 半导体学报, Journal of Semiconductors, 编辑部邮箱 2008年 08期  
8 c" F8 A+ N" J. L4 @7 G期刊荣誉:中文核心期刊要目总览  ASPT来源刊  中国期刊方阵  CJFD收录刊
' R2 D3 U4 _4 l+ a: p【关键词】 a-Si薄膜; 退火; 晶化; AIC;
1 ?. J. ^) I) s% t$ S# T8 z4 G【英文关键词】 a-Si film; annealing; crystallization; AIC; * \2 q5 H/ K7 Q, R$ k3 u8 p/ L
【摘要】 以玻璃为衬底,室温条件下采用直流磁控溅射技术制备了Glass/Al/a-Si样品.在H2,N2和空气3种不同气氛中进行了退火处理.分别采用XRD,Raman光谱和SEM研究了退火气氛对a-Si薄膜铝诱导晶化(AIC)过程的影响.XRD实验结果表明:a-Si薄膜在H2气氛中400℃下经过90min的退火处理就能得到结晶较好的poly-Si薄膜.Raman光谱实验结果表明:在500℃下退火处理,相同时间内H2气氛中a-Si结晶程度最好,空气气氛中结晶程度最差.这是因为高温H2退火过程中,高活性H原子能将弱的Si—Si键破坏,并与之反应形成强Si—Si键,使得薄膜结构更加稳定有序,同时能加速薄膜中氧的外扩散,促使薄膜晶化.
6 b$ ^6 Q6 U6 T4 C+ O7 ~3 G【英文摘要】 The influence of annealing atmosphere on the aluminum-induced crystallization(AIC)of a-Si film has been studied by X-ray diffraction spectroscopy,Raman spectroscopy,and scanning electron microscopy.The films were annealed in different annealing atmospheres,i.e.,H2,N2 and air.The Al and amorphous silicon films were deposited by DC magnetron sputtering on glass substrate.The XRD results indicate that the a-Si film was crystallized to poly-Si when the sample was annealed in H2 at 400℃ for 90min.The results of ... 9 @) m: Q$ |: \/ v4 D' Q: U
【基金】 国家高技术研究发展计划(批准号:2006AA04Z322);; 教育部长江学者与创新团队计划(批准号:IR0629);; 国家自然科学基金(批准号:50505037,60676033);; 兰州交通大学“青蓝”人才工程资助项目~~

本帖子中包含更多资源

您需要 登录 才可以下载或查看,没有帐号?注册

x
您需要登录后才可以回帖 登录 | 注册

本版积分规则

本站邀请注册说明!

小黑屋|手机版|Archiver|光学薄膜信息网  

GMT+8, 2024-6-15 11:04 , Processed in 0.039110 second(s), 19 queries .

Powered by Discuz! X3.4 Licensed

Copyright © 2001-2021, Tencent Cloud.

快速回复 返回顶部 返回列表