A Patterned Coating
A Patterned Coating[A patterned coating (also known as a nonuniform coating) has a layer structure that is different on different areas of the substrate. For example, in the top-view shown below, the three shadings represent three different coatings on the same substrate.
http://www.sspectra.com/designs/patrn1.gif
Patterned coatings have applications in such diverse areas as LCD displays, detector systems, and color filters. The manufacturing process for these coatings has much in common with the manufacture of semiconductor "chips". Although it is possible for the coatings to be completely different in the three areas, the designs for the three areas usually have one or more layers in common. The diagram below shows a side-view of the three designs.
http://www.sspectra.com/designs/patrn2.gif
The challenge is to design the three coatings so that they have the desired reflectance, transmittance, etc. Designers can use TFCalc's multiple environments and active materials features to create these coatings.
To illustrate this method of design, we seek to create a patterned coating consisting of four areas. The goal is to create areas that reflect three quite different colors when illuminated by white light. This patterned coating will be manufactured as follows:
Mask part of the glass substrate
Deposit a number of layers -- coating A
Remove the mask and apply another mask
Deposit a number of layers -- coating B
Remove the mask This procedure will create a glass substrate having areas covered by (1) coating A, (2) coating B, (3) coatings A and B, or (4) no coating. TFCalc is used to design the A, B, and A+B coatings simultaneously. All of the coatings will consist of alternating layers of SIO2 and TIO2.
In TFCalc, we use the multiple environments capability to create an environment for each of the three coatings: A+B, A, and B. The environments have two uses. They enable us to specify the performance requirements for each coating. They also let us specify how layers are transformed when we switch environments. Below is a screen shot of the Environments window.
http://www.sspectra.com/designs/patrn3.gif
Much of the information in the Environment window is the same as in the Environment window. However, note the four active material rows. These describe how a layer's material changes in the three environments. Before creating these environments, we added new materials called SIO2-2, TIO2-2, GLASS, GLASS-2, AIR, and AIR-2 having the same indices as SIO2, TIO2, GLASS, and AIR. The first column, environment 1, represents the design for A+B. The second column, environment 2, represents the design for B; it says that the SIO2 and TIO2 layers should be replaced by GLASS and GLASS-2. The third column, environment 3, represents the design for A; it says that the SIO2-2 and TIO2-2 layers should be replaced by AIR and AIR-2.
Next, we specify the performance targets for each of the A, B, and A+B coatings. The reflected color targets are as follows:
A x=0.6 y=0.3 Y > 20% (reddish color)
B x=0.15 y=0.15 Y > 20% (bluish color)
A+B x=0.35 y=0.2 Y where Y is the luminosity. We specify Y(A+B)
As the starting design for the A+B coating, we use H(LH)^8 (XY)^8, where H=TIO2, L=SIO2, X=SIO2-2, and Y=TIO2-2. All of the thicknesses are 0.8 QWOT at the 550 nm reference wavelength.
Finally, we are ready to start optimizing. Because local optimization would quickly find only an inferior local minimum, we opt to use TFCalc's global search capability. We quickly scan 10000 random designs to find a set of possible designs. Then local optimization is used to refine the possible designs. We find a 26-layer design that comes close to meeting all of the performance requirements. The performance is shown below.
http://www.sspectra.com/designs/patrn5.gif
The design of A+B, starting with the layer closest to the substrate, and with thicknesses given in nm is:
TIO2 96.06
SIO2 309.82
TIO2 86.00
SIO2 101.20
TIO2 85.36
SIO2 116.96
TIO2 98.20
SIO2 35.68
TIO2 76.30
SIO2 154.25
TIO2 60.90
SIO2 80.80
SIO2-2 104.66
TIO2-2 51.04
SIO2-2 65.40
TIO2-2 31.22
SIO2-2 78.34
TIO2-2 51.39
SIO2-2 223.80
TIO2-2 38.13
SIO2-2 53.69
TIO2-2 29.70
SIO2-2 64.75
TIO2-2 48.04
SIO2-2 71.99
TIO2-2 14.36
The design can be improved by making some small changes and reoptimizing: (1) reduce the thickness of layer 2 by 2 QWOTs (189 nm) and (2) remove the thin last layer.
Download DesignYou may download the final design. To work with this design, the real version of TFCalc is required. Click here for the Windows zip file containing the design and the materials it requires. Use Windows Explorer to move the materials into TFCalc's "MATERIAL" directory.